1018 Cold Rolled Steel Coil1018 cold rolled steel coil is made of a general-purpose, low-carbon steel with good case hardening qualities. It is especially suited tocold forming and bending operations. 1018steelis suitable for parts that require cold forming such as crim
Opening Hours: Monday - Saturday 8 am to 7 pm
- Time Office:
Monday to Friday 8:00am - 7:00pm
- Call Us:
+86 13396253653
- Email:
admin@sdyulun.com
Carbon Steel Coil
1018 Cold Rolled Steel Coil
- Date.October 31, 2024
- Category.Carbon Steel Coil
- Keyword.Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
1018 Cold Rolled Steel Coil
1018 cold rolled steel coil is made of a general-purpose, low-carbon steel with good case hardening qualities. It is especially suited to cold forming and bending operations. 1018 steel is suitable for parts that require cold forming such as crimping, swaging, or bending. 1018 steel is mild steel with medium-low carbon content. AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world. Although its mechanical properties are not very unique, it still can be easily formed, machined, welded and fabricated.
Product Parameters
Product Name | 1018 Cold Rolled Steel Coil |
Production Process | Hot Rolling, Cold Rolling |
Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
Width | 100mm-3000mm |
Length | 1m-12m, or Customized Size |
Thickness | 0.1mm-400mm |
Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Manganese, Mn | 0.60-0.90 |
| Carbon, C | 0.15-0.20 |
| Sulfur, S | 0.05 (max) |
| Phosphorous, P | 0.04 (max) |
| Iron, Fe | Balance |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 440 MPa | 63800 psi |
| Yield strength | 370 MPa | 53700 psi |
| Modulus of elasticity | 205 GPa | 29700 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poisson’s ratio | 0.29 | 0.29 |
| Elongation at break (in 50 mm) | 15 % | 15 % |
| Hardness, Brinell | 126 | 126 |
| Hardness, Knoop (converted from Brinell hardness) | 145 | 145 |
| Hardness, Rockwell B (converted from Brinell hardness) | 71 | 71 |
| Hardness, Vickers (converted from Brinell hardness) | 131 | 131 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 70 | 70 |
Scope of Application
AISI 1018 carbon steel is commonly used in high volume screw machine parts applications. The other applications of this alloy are as follows:
● Shafts
● Spindles
● Pins
● Rods
● Sprocket assemblies.
Mark Doe
Galvanized coils are our top choice for durability and
consistency.
The zinc layer
uniformity saves us time in post-processing, and your team's technical
support is
always
helpful.
Mahan Selon
We have been purchasing yulun galvanized steel coils for
the quality
has
consistently exceeded our expectations. The coating uniformity, corrosion
resistance, and
surface finish meet our strict standards, making them ideal for
construction.